Spin dynamics, electrical and magnetic properties of (La0.5Pr0.5)(0.7)Pb0.3Mn1-xCuxO3 (x=0, 0.02) perovskites
T.L. Phan
N.D. Tho
M.H. Phan
N.D. Ha
N. Chau
S.C. Yu
N.D. Tho
M.H. Phan
N.D. Ha
N. Chau
S.C. Yu
Magnetization, resistivity, and electron spin resonance (ESR)
measurements were carried out to investigate spin dynamics, electrical
and magnetic properties of (La0.5Pr0.5)(0.7)Pb0.3Mn1-xCuxO3 (x = 0,
0.02) perovskites. It was found that with Cu addition the Curie
temperature decreased from 326 K for x = 0 to 300 K for x = 0.02
composition. The x = 0 sample underwent a metallic-insulator transition
at similar to 130 K, whereas the x = 0.02 sample with higher resistivity
exhibited ail insulating behavior as a whole. It was furthermore found
that asymmetrical ESR signals at low temperatures became Lorentzian at
high temperatures above T-min. The temperature dependence of the
linewidth, Delta H(T), at T > T-min fits well to the one-phonon
model, Delta H(T) = AT + B. The activation energy E, determined from the
ESR intensity with respect to temperature, are 0.16 and 0.14 eV for x =
0 and 0.02 compositions, respectively. In terms of our experimental
results, it is reasonable to conclude that the Cu addition led to a
suppression of the ferromagnetism and conductivity of the parent
compound (x = 0).
Chi tiết xin mời tham khảo tại http://repository.vnu.edu.vn/handle/VNU_123/31994
Title: | Spin dynamics, electrical and magnetic properties of (La0.5Pr0.5)(0.7)Pb0.3Mn1-xCuxO3 (x=0, 0.02) perovskites |
Authors: | T.L. Phan N.D. Tho M.H. Phan N.D. Ha N. Chau S.C. Yu |
Keywords: | perovskite manganites;magnetic and electrical properties;ESR |
Issue Date: | 2006 |
Publisher: | ELSEVIER SCIENCE BV, PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS |
Citation: | ISIKNOWLEDGE |
Description: | PHYSICA B-CONDENSED MATTER Volume: 371 Issue: 2 Pages: 317-322 Published: JAN 31 2006 ; TNS07719 |
URI: | http://www.sciencedirect.com/science/article/pii/S0921452605011683 http://repository.vnu.edu.vn/handle/VNU_123/31994 |
ISSN: | 0921-4526 |
Appears in Collections: | Bài báo của ĐHQGHN trong Web of Science |
Nhận xét
Đăng nhận xét